Industry Developments: Extrusion Profile Heat Sinks

Extruded metal heat sinks are among the lowest cost, widest used heat spreaders in electronics thermal management. Besides their affordability, extruded heat sinks are lightweight, readily cut to size and shape, and capable of high levels of cooling.

Most extruded heat sinks are made from aluminum alloys, mainly from the 6000 alloy series, where aluminum dominates. Trace amounts of other elements are added, including magnesium and silicon. These alloys are easy to extrude and machine, are weldable, and can be hardened.

Common alloys for extruded heat sinks are the 6063 metals. These can be extruded as complex shapes, with very smooth surfaces. 6061 aluminum is also used for extrusions. Its tensile strength (up to 240 MPa) is superior to 6063 alloys (up to 186 MPa). In addition to heat sinks, these aluminum alloys are popular for architectural applications such as window and door frames. 

The surfaces of these metals can be anodized to replace their naturally occurring surface layer of aluminum oxide. Anodizing provides more heat transfer, corrosion resistance and better adhesion for paint primers. It is an electrochemical process that increases surface emissivity, corrosion and wear resistance, and electrical isolation.

The Extruding Process

Aluminum alloys are popular for extruding as heat sinks because they provide both malleability and formability. They can be easily machined and are as little as one-third the density of steel. This results in extrusions that are both strong and stable, at a reduced cost relative to other materials.

The aluminum extrusion process starts with designing and creating the die that will shape the heatsink extrusion. Once this has been done, a cylindrical billet of aluminum is heated up in a forge to high temperatures, generally between 800-925°F (427-496°C). Next, a lubricant is added to the aluminum to prevent it from sticking to any of the machinery. It is then placed on a loader and pressure is applied with a ram to push heated aluminum through the die.